[1]张圳炫,荣守范,李洪波,等.局部水淬耐磨钢犁铧研究与应用[J].哈尔滨理工大学学报,2019,(04):94-98.[doi:10.15938/j.jhust.2019.04.016]
 ZHANG Zhen-xuan,RONG Shou-fan,LI Hong-bo,et al.Research and Application of Local Water Quenched Wear-Resistant Steel Plough[J].哈尔滨理工大学学报,2019,(04):94-98.[doi:10.15938/j.jhust.2019.04.016]
点击复制

局部水淬耐磨钢犁铧研究与应用()
分享到:

《哈尔滨理工大学学报》[ISSN:1007-2683/CN:23-1404/N]

卷:
期数:
2019年04期
页码:
94-98
栏目:
材料科学与工程
出版日期:
2019-08-25

文章信息/Info

Title:

Research and Application of Local Water Quenched Wear-Resistant Steel Plough
文章编号:
1007-2683(2019)04-0094-05
作者:
张圳炫1荣守范1李洪波1王迪1焦仁宝1刘力1孙柯楠1王俊发2
(1.佳木斯大学 材料科学与工程学院,黑龙江 佳木斯 154007; 2.佳木斯大学 机械工程学院,黑龙江 佳木斯 154007)
Author(s):
ZHANG Zhen-xuan1RONG Shou-fan1LI Hong-bo1WANG Di1JIAO Ren-bao1LIU Li1SUN Ke-nan1WANG Jun-fa2
(1.School of Material Science and Engineering,Jiamusi University,Jiamusi 154007,China;
2.School of Mechanical Engineering, Jiamusi University,154007,China)
关键词:
碳含量水淬空淬耐磨性
Keywords:
carbon content water quench air quench wear resistance
分类号:
TG161
DOI:
10.15938/j.jhust.2019.04.016
文献标志码:
A
摘要:
针对高锰钢犁铧耐磨性较差,为了提高犁铧的韧性及耐磨性,降低犁铧的断裂与磨损,在改变碳元素的基础上研究淬火方式对耐磨钢的组织与性能的影响。结果表明:随着碳含量升高,局部水淬/空淬钢的硬度逐渐升高,而冲击韧性逐渐降低。碳含量为0.344%,热处理工艺为“940℃淬火×1.5h+局部水冷/空冷+200℃×3h回火”试验钢的综合力性能最好,水淬部分硬度为49HRC,冲击韧性ak值为145J/cm2;空淬部分硬度为30HRC,冲击韧性ak值为260J/cm2。经过装机应用试验,局部水淬/空淬钢材质犁铧的使用寿命是高锰钢材质犁铧的2~3倍。
Abstract:
In view of the poor wear resistance of high manganese steel ploughshare, in order to improve the toughness and wear resistance of ploughshare and reduce the fracture and wear of ploughshare, the influence of quenching method on the microstructure and properties of wearresistant steel was studied on the basis of changing carbon elements.The results show that with the increase of carbon content, the hardness of local water quenching/air quenching steel increases gradually, and the impact toughness decreases gradually. The carbon content is 0.344%, and the heat treatment process is “940℃ quenching×1.5h+local water cooling/air cooling+200℃×3h tempering”.The test steel has the best comprehensive performance. The hardness of the water quenching part is 49HRC, and the impact toughness ak value is 145J/cm2; the hardness of the air quenching part is 30HRC, and the impact toughness ak value is 260J/cm2. ?After the installation application test, the service life of the local water quenching/air quenching steel material plough is 2~3 times as long as that of the high manganese steel material ploughshare.

参考文献/References:

[1]白智辉, 高峰, 王大峰. 不同颗粒度碳化钨的WC17Co等离子涂层组织及摩擦学特性研究[J]. 热喷涂技术, 2015, 7(3):48.
[2]邓锋, 胡锋, 吴开明. 低合金高强度耐磨钢的发展与应用[J]. 金属材料与冶金工程, 2016, 44(2):29.
[3]罗晔, 薛思毅, 袁宇峰. 国内外低合金耐磨钢生产概况[J]. 冶金管理, 2013(11):20.
[4]李文斌, 费静, 曹忠孝, 等. 我国低合金高强度耐磨钢的生产现状及发展方向[J]. 机械工程材料, 2012, 36(2):6.
[5]张圳炫, 荣守范, 刘会. 中高碳贝氏体钢耐磨犁铧的研究[J]. 佳木斯大学学报(自然科学版), 2018, 36(1):86.
[6]陈德东, 李卫. 低合金耐磨铸钢的研究与应用[J]. 金属铸锻焊技术, 2011, 40(11):17.
[7]赵培峰, 国秀花, 宋克兴. 高锰钢的研究与应用进展[J]. 材料开发与应用, 2008(4):85. 
[8]张峰, 樊飞. 碳钢及低合金钢制压力容器母材热处理试件与产品焊接试件是否合并的选择[J]. 石油和化工设备, 2016, 19(12):48. 
[9]张圳炫, 荣守范, 焦仁宝, 等. 热处理工艺对中碳贝氏体钢组织与性能的影响[J].铸造设备与工艺,2018(4):28.

备注/Memo

备注/Memo:
?收稿日期: 2019-01-02
基金项目: 国家自然科学基金(51371090,51875252);黑龙江省大学生创新创业训练计划项目(201710222025)
作者简介:
张圳炫(1993—),男,硕士研究生;
李洪波(1977—),男,副教授
通信作者:
荣守范(1956—),女,教授,博士研究生导师,E-mail:rsfzz@163.com
更新日期/Last Update: 2019-09-03